聚氨酯浇注树脂
聚氨酯树脂的原材料种类广，通过配方的调整可以开发出不同性能的产品，从软质的弹性体到硬质的塑料，操作时间和反应速度也可以灵活的调整，具有非常广泛的应用。针对模型模具行业的应用，艾普科开发出了多款聚氨酯浇注树脂，在弹性体、陶瓷模具、铸造模具、金属成型模具等行业得到广泛应用。
| Resin/Hardener 树脂/固化剂 |
Pot-life 操作时间 |
Mix ing ratio 混合比 |
Properties 特性 |
Applications 应用 |
Download 下载 |
| PuCast 145 | 15-25 min | 100/12 | shore A45 hardness, high tear strength, well castable 邵A45硬度，抗撕裂，易浇注 |
casting mould for gypsun, plastic, wax, ceramic material 石膏、塑料、蜡和陶瓷材料的浇注模具 |
TDS |
| PuCast 190 | 12-15 min | 100/15 | shore A90 hardness, high tear strength, well castable, flexible 邵A90硬度，抗撕裂，易浇注，弹性高 |
flexible parts, jigs 弹性部件，夹具 |
TDS |
| PuCast 260 | 50 min | 100/75 | good flowability of unfilled resin, high abrasion and impact resistance, high filler possible 不加填料的树脂流动性好，耐磨性和抗冲击性好，可加入填料 |
face casting layer for metal sheet forming tools and foundry patterns 金属板成型模具和铸造模型的表面浇注 |
TDS |
| PuCast 265 | 60 min | 100/100 | slow curing for large part casting, high filler possible 固化速度慢，可做大型浇注，可以加入填料 |
sheet metal forming, foundry pattern, negatives 金属板成型模具，铸造模型 |
TDS |
| PuCast F14 | 5 min | 100/100 | low viscosity, good temperature resistance after thermal treatment 低粘度，加入固化后耐温性好 |
thickness up to 40mm; foundry patterns; negatives; vacuum forming moulds | TDS |
| PuCast F40 | 5 min | 100/20 | excellent abrasion resistance, low shrinkage, low viscosiy. 优异的耐磨性，低收缩，低粘度 |
core boxes, fountry patterns, reproduction patterns 砂芯盒，铸造模型 |
TDS |
| PuCast F16 | 2min30sec | 100/100 | Rapid demouding, good temperature resistance after curing, easy to paint 快速脱模，加入固化后耐温性好，表面可喷漆 |
negatives, patterns, models, vacuum forming moulds 铸造模型，真空成型模 |
TDS |
| PuCast F18 | 3min30sec | 100/100 | good impact resistance, excellent mechanical property 抗冲击性好，力学性能优异 |
negatives, patterns, models, vacuum forming moulds 铸造模型，真空成型模 |
TDS |
| PuCast F19 | 7 min | 100/100 | very low shrinkage, long pot life 收缩率非常低，操作时间长 |
negatives, patterns, models, vacuum forming moulds 铸造模型，真空成型模 |
TDS |
| PuCast F31 | 2 min | 100/100 | rapid demoulding, good substrate for painting 快速脱模，表面质量好，可喷漆 |
prototyping up to 5mm thickness, scale models 可进行5mm厚的复模浇注，可批量浇注 |
TDS |
| PuCast F38 | 2 min | 100/100 | excellent impact resistance, low viscosity, good substrate for pianting 优异的抗冲击性，低粘度，表面质量好，可喷漆 |
production of models and prototypes for extremely detailed parts 可浇注精细的复模件 |
TDS |
| PuCast F202 | 1min45sec | 100/100 | opaque even in small thickness, fast demoulding, good ability to be painted, good UV resistance, low chemical attack towards silicone mould 即使薄壁也不透明，快速脱模，可喷漆，耐紫外线，对硅胶的腐蚀性小 |
casting of prototypes and small-scale models in silicone moulds 在硅胶模具中复模浇注和小批量浇注 |
TDS |